Wood Anatomy and Physical and Mechanical Properties of Toona sinensis (Meliaceae)

 ZHANG  You-Yuan-1, XIA  Yu-Fang-2   

  1. 1 Centre for Mountain Ecosystem Studies, Kunming Institute of Botany, Chinese Academy of Sciences,
    Kunming 650201, China; 2 Guizhou University, College of Forestry, Guiyang 550025, China
  • Received:2012-12-24 Online:2013-09-25 Published:2013-04-02
  • Supported by:

    贵州省林业厅项目“香椿人工林多用途效益研究” (2006-15)

PDF (PC)

1665

Cited

4

Abstract:

 Research on Toona sinensis is important for its cultivation in China and provision of a highquality timber resource. We used the GB1927-91 Test Method to examine the anatomy and  physicomechanical properties of Toona sinensis wood. We found that fiber morphology is shaped, on average, after 13 years of growth, with an aspect ratio of 46.18, double wall thickness of 11.00μm, fiber wall cavity ratio of 0.56, and cavity diameter ratio of 0.76. Average length and width of vessel elements was 383.52μm and 143.98μm, respectively, basic density was 0.415g/cm3 and air dry density was 0.475g/cm3. The wood may be described as a “light and low type” timber with differences in shrinkage of 1.93, wood bending strength, modulus of elasticity and compressive strength of grain rolls of 67.85MPa, 6179.82MPa and 38.23MPa, respectively, an integrated strength of 106.08MPa, and a comprehensive quality factor of 2556.1×105Pa. Based on our findings, Toona sinensis may be considered to produce a form of high-quality wood.

Key words: Toona sinensis, Wood anatomy, Physical properties, Mechanical properties